- Chemical Auxiliary Agent[4]
- Alkali[1]
- Organic Intermediate[7]
- Other Chemicals[2]
- Polymer[10]
- Cement Boards[1]
- Sandwich Panels[1]
- Metal Building Materials[1]
- Other Construction Material Making Machinery[2]
- Mixing Equipment[1]
- Other Construction Machinery[1]
- Wire EDM Machine[1]
- Other Metal Processing Machinery[10]
- Other Machinery[1]
- Packaging Machinery[2]
- Other Plastic Processing Machinery[3]
- Plastic Blowing Machinery[1]
- Plastic Extruders[1]
- Plastic Granulators[1]
- Plastic Vacuum Forming Machinery[2]
- Plastic Product Making Machinery[6]
- Fiberglass Mesh[5]
- Protective & Cushioning Material[2]
- Other Plastic Products[10]
- EPS[4]
- Other Plastic Raw Materials[1]
- Contact Person : Mr. zhu huadong
- Company Name : Jiangyin City Sunping Chemical Co., Ltd.
- Tel : 86-0510-81602871,2,3
- Fax : 86-0510-81602933
- Address : Jiangsu,jiang yin,room 1101a huifeng mall,NO.4shashan.RD
- Country/Region : China
- Zip : 214400
HIGH IMPACT POLYSTYRENE
Related Product Searches:HIGH IMPACT POLYSTYRENE,High Quality,HIPS raw material, high impact polystyrene,HIPS
High Impact Polystyrene HIPS 5.0
Characteristics
_ Super High Impact Strength
_ Low Residual Monomer
_ Good Heat Resistance
_ Base Color Stability
_ Good Transparency
_ Easy Processing
_ High Flow
Applications
Electrical appliances, toys, Comply with the food sanitation standards .etc
Physical Properties
Prosperities | Test Condition | Test Method | Value | Unit |
Melting Flow Rate | 200°C/5kg | ISO 1133 | 5.0 | g/10min |
Density | ISO 1183 | 1.04 | g/cm3 | |
Water Absorption | ISO 62 | <0.1 | % | |
Molding Shrinkage | ISO 294 | 0.4-0.7 | % | |
Tensile Strength | 23°C | ISO 527 | 23 | Mpa |
Tensile Elongation | 23°C | ISO 527 | 50 | % |
Flexural Strength | 23°C | ISO 178 | 46 | Mpa |
Flexural Modulus | 23°C | ISO 178 | 2260 | Mpa |
Izod Impact Strength | 23°C | ISO 180 | 108 | j/m |
Rockwell Hardness | 23°C | ASTMD-785 | 65 | L |
Vicat Softening Temp. | B10/oil | ISO 306 | 95 | °C |
Heat Distortion Temp. | 1.82Mpa | ISO 75-2 | 79 | °C |
UL Flame Class Rating | UL 94 | HB | ||
Residual Monomer | <400 | ppm max |
HIGH IMPACT POLYSTYRENE